YAP.HARCI Megaflex Granit BEYAZ KÜTAHYA 25 kg

Initial tensile adhesion strength: ≥ 1 N / mm² (EN 12004-2: 2017, 8.3)
tensile adhesion strength after immersion in water: ≥ 1 N / mm² (EN 12004-2: 2017, 8.3)
In the tensile adhesion strength after immersion ≥ 1 N / mm² (EN 12004-2: 2017, 8.3)
Freeze - tensile adhesion strength after thaw cycles: ≥ 1 N / mm² (EN 12004-2: 2017, 8.3)
Tensile adhesion strength after open time (30 min. After): ≥ 0.5 N / mm² (EN 12004-2: 2017, 8.1)
Transverse strain S2 ≥ 5 mm (EN 12004-2: 2017, 8.6)
Slip: ≤ 0.5 mm (EN 12004-2: 2017, 8.2)
Fire response class: A1 (TS EN 13501 - 1)

These values under laboratory conditions; 23 ± 2 ° C and 50 ± 5% relative humidity experiments on the environment has been obtained as a result. The values given above may vary depending on the substrate and ambient conditions.

Usability time of the ready mortar - Pot life: Up to 3 hours
Work life: Maximum 30 minutes.
Adjustment time: 15 min.
The time required for joint applications: 24 hours
The time required for the opening to traffic of the floor: 24 - 48 hours

These values under laboratory conditions; 23 ± 2 ° C and 50 ± 5% relative humidity experiments on the environment has been obtained as a result. The values given above may vary depending on the substrate and ambient conditions.

a. Chemical Structure: Cement-based, polymer additive, ceramic adhesive mortar
b. Dry Density: 1.35 ± 0.05 g / cm³
c. Mortar Density: 1.75 ± 0.05 g / cm³
D. Grain Size: ≤ 600 .mu.m
to. Color: Gray, White
f. Temperature Range: -15 ° C and + 80 ° C

Wt% 22 - 26 to be mixed with water in the ratio. (5.5 to 25 kg packing - 6.5 liters of water)

10x10 cm and 10x15 cm and smaller ceramic dimensions, 6x6x6 with scallops
One-sided adhesive: 4,0 - 4,5 kg / m²
Double-sided adhesive: 5.0 - 5.5 kg / m²

from 10x15 to 25x40 cm, 10x15 cm and 33x33 ceramic dimensions, 8x8x8 with scallops
One-sided adhesive: 4.5 to 5.0 kg / m
Double-sided adhesive: 6,0 - 6,5 kg / m²

25x40 33x33 cm size on top of ceramic, 10x10x10 with scallops
One-sided adhesive: 5.0 - 5.5 kg / m²
Double-sided adhesive: 6.5 to 7.0 kg / m

MEGAFLEX; A total of 54 bags of 25 kg net paper bags 80x100 cm measured pallet (1350 kg) are presented.

a. Approvals / Standards
• EN 12004
b. Look Works. Exposure No.
• Public Look. Item No .: 04 013/1
• Public Look. Item No .: 04 013/4

QUALITY CERTIFICATES
• EN 12004 / C2TES2
• CE
• EPD

Substrates
Interior and Exterior Wall;
• cement based plasters
• Concrete (MEGAFILM A201 or A204 primed MEGAFILM BB)
• Old ceramic coating (MEGAFILM Viscose primed A203)
Interior and Exterior Floor;
• cementitious screeds
• Concrete (MEGAFILM A201 or A204 primed MEGAFILM BB)
• Old ceramic coating (MEGAFILM Viscose primed A203)

Surface Preparation
• Surface dry, clean, solid and must be free from dust, oil, dirt or adhesion inhibiting materials from the surface to be cleaned, slurry, binders such as cement residues scraped.
• dusty surfaces should be cleaned behind the tiles with water.
• Depth 6 for implementing error repair adhesive mortar surface which is more than 1 cm - 8 hours before megatam megatam K should be done by IR T101 or T102. Megatam structural mortar is used in cases where the structural T103 or T104 structural megatam K should be used.
• After surface cleaning, surface to compensate for the increase of adhesive strength and absorbency of the substrate should be primed with single coat MEGAFILM A201 lining and 1 - 2 hours should be allowed to dry.
• Gross before being put into practice in order to increase the adhesive strength concrete surface should be primed with single coat A204 MEGAFILM BB concrete lining and the minimum should be allowed to dry for 3 hours.
• ceramic tiles on old ceramic coating as a primer before MEGAFILM Viscose primed with single coat primer A203 and minimum should be allowed to dry for 3 hours.
• Wet embodiments of the primed surface with the recommended primer before tire 10 water insulation with ceramic tiles megaizo S103 products must be provided.

Application Methods
• MEGAFLEX Y103 adhesive mortar, determined according to the structural condition of the ceramic size and the surface is applied with a notched trowel.
• MEGAFLEX Y103's surface during application must be careful not to create the film. Adhesive film was scraped form the surface of the ground and be reused.
• placing the coating material to the surface, tire seating surfaces should be provided with a pointed knob.
• grouting process, the bonding process should be started after at least 24 hours.
• Indoor and outdoor applications for large-format double-sided coating applications from 33x33cm paste should be applied.
• deleting in the exterior coat applications up to 8 m high vertical profile supported 45x45 cm tile pasted.

Practice Recommendations
• It is recommended that the light-colored wall and floor ceramic bonding with white MEGAFLEX Y103.
• After the mixed product must be used within the pot life. have filled the pot-life products should not be used during application.
• prepared mortar of lime, cement, not add any foreign material, such as plaster.
• extra water mixture must be topped up.
• Do not apply on solid surfaces. strength of the former surface and the carrier before the application process should be controlled.
• Application during and after the surface must be protected from contact with water and air flow must be prevented.
• The risk of frost within 24 hours, should not be applied on surfaces which are frozen or ice melt.
• Attention should be paid to exposure to direct sunlight in hot weather the material should be done with cold water and mix.
• Excessive wind should not be applied on hot surfaces or direct sun-exposed, media before practice if necessity in these environments, and should be ready for surface applications.
• In rainy weather application must be made, the application must be protected from rain with surface for 24 hours.
• You can call our technical support line at various surface treatments. (TEL: 444 4595)

Surface and Ambient Temperature
During the application surface and ambient temperature should be between + 5 ° C and + 35 ° C.